PBAT is a biodegradable thermoplastic, which is a copolymer of butylene adipate and butylene terephthalate. It has the characteristics of PBA and PBT, and has good ductility and elongation at break, as well as good heat resistance and impact performance. In addition, it also has excellent biodegradability, and is currently one of the very active and market application degradable materials in biodegradable plastic research.

PBST (polybutylene terephthalate resin) is a copolyester polymerized from monomers of sebacic acid, terephthalic acid and butanediol. PBSA is a biodegradable plastic that can be degraded by microorganisms in natural environment. The decomposition rate in 180 days under composting conditions is higher than 90%.

PBSA (polybutylene succinate/butylene adipate) is a semi-crystalline copolyester polymerized by monomers of succinic acid (SA), adipic acid (AA) and butanediol (BDO). Its appearance is milky white and light yellow particles. PBSA is a biodegradable plastic that can be degraded by microorganisms in natural environment. The decomposition rate in 180 days under composting conditions is higher than 90%.

PBS (polybutylene succinate) is a thermoplastic polyester and is a fully biodegradable resin produced by continuous polymerization of succinic acid (SA) and butanediol (BDO). The resin is milky white, odorless and tasteless, excellent mechanical properties, good heat resistance, thermal deformation temperature and product use temperature can exceed 100°C, has good biocompatibility and bioabsorbability, and is easy to be used in nature A variety of microorganisms or enzymes in animals and pla

PBAT is a thermoplastic biodegradable plastic. It is a copolymer of butylene adipate (BDO), adipic acid (AA), terephthalic acid (PTA) or terephthalate (DMT) as raw materials and is prepared by direct esterification or transesterification. It has the characteristics of PBA and PBT. According to the source of raw materials, PBAT belongs to petrochemical-based biodegradable plastics.
PBAT is a semi-crystalline polymer, usually the crystallization temperature is around 110 ℃.